Polypropylene
Low moisture absorption and high stiffness make polypropylene suitable for manufacturing strong, long-lasting products.
Features
Polypropylene offers good processability thanks to its low density and high crystallinity. Its low moisture absorption and high stiffness make it suitable for producing robust, long-lasting products. Homopolymer polypropylene (PPH) can be used in injection molding, extrusion and thermoforming, notably for rigid packaging, pipes, sheets and automotive components.
Detailed Information
Technical Specifications & Options
Polypropylene Moplen HP550J (Fibre)
| TYPICAL PROPERTIES | TEST METHOD (ASTM) | UNITS | VALUE |
|---|---|---|---|
| MFR at 230°C, 2.16 kg | D1238/L | gr/10min | 3 |
| Flexural Modulus | D790 | MPa | 1350 |
| Notched Izod Impact at 23°C | D256 | J/m | 35 |
| Tensile Strength at Yield | D638 | MPa | 35 |
| Elongation at Yield | D638 | % | 12 |
| Vicat Softening Point, 10 N | D1525 | °C | 156 |
| Heat Deflection Temperature (0.46 N/mm²) | D648 | °C | 94 |
| Rockwell Hardness | D785 | R.Scale | 102 |
| Oven Aging at 150°C | D3012 | Hours | 360 |
Polypropylene Moplen HP552R (Fibre)
| TYPICAL PROPERTIES | TEST METHOD (ASTM) | UNITS | VALUE |
|---|---|---|---|
| MFR at 230°C, 2.16 kg | D1238/L | gr/10min | 25 |
| Flexural Modulus | D790 | MPa | 1500 |
| Notched Izod Impact at 23°C | D256 | J/m | 30 |
| Tensile Strength at Yield | D638 | MPa | 32 |
| Elongation at Yield | D638 | % | 13 |
| Vicat Softening Point, 10 N | D1525 | °C | 152 |
| Heat Deflection Temperature (0.46 N/mm²) | D648 | °C | 94 |
| Rockwell Hardness | D785 | R.Scale | 100 |
| Oven Aging at 150°C | D3012 | Hours | 150 |
Phone
+90 212 465 60 11Monday - Friday, 08:00 - 18:00
Email Address
info@phoenixpolimer.comWe will get back to you as soon as possible.
Address
Kayabaşı Mah. Kayaşehir Blv. Nidakule No:45 Kat:12 D:74-75 Başakşehir / İstanbulOur Head Office
Müşteri Hizmetleri
+90 212 465 60 11Get information about our products.